无机玻璃钢风管的的分类介绍
无机玻璃钢风管按其胶凝材料性能分为:以硫酸盐类为胶凝材料与玻璃纤维网格布制成的水硬性无机玻璃钢风管和以改性氯氧镁水泥为胶凝材料与玻璃纤维
The properties of inorganic glass steel wind pipe are divided into water hard inorganic glass steel wind pipe made of sulfate as cementitious material and glass fiber mesh cloth and modified magnesium oxychloride cement as cementitious material and glass fiber
网格布制成的气硬性改性氯氧镁水泥风管两种类型。胶凝材料硬化体的PH值
Two types of pneumatic modified magnesium oxychloride cement pipes made of mesh cloth. The pH value of the hardened body of a cementitious material
应小于8.8,并不应对玻璃纤维有碱性腐蚀。
Should be less than 8.8, should not be alkaline corrosion of glass fiber.
      
      
无机玻璃钢风管应采用无碱、中碱或抗碱玻璃纤维网格布,并分别符合现
Inorganic glass fiber reinforced plastic pipes should be made of alkali free, medium alkali or alkali resistant fiberglass mesh fabrics.
行国家标准《玻璃纤维网格布》JC561、《无碱玻璃纤维、无捻粗纱布》JC/T281、《中碱玻璃纤维无捻粗纱布》JC/T576的规定。氯氧镁水泥风管氧化镁的品质应符合现行国家标准《菱镁制品用轻烧氧化镁》WB/T1019-2002的规定。
The provisions of the national standard "glass fiber mesh cloth" JC561, "alkali free glass fiber, non twisting coarse gauze" JC/T281, "middle alkali glass fiber coarse gauze" JC/T576. The quality of Magnesium Oxide magnesium oxychloride cement pipe should conform to the current national standard "magnesia products light burn Magnesium Oxide" WB/T1019-2002.
无机玻璃钢风管分为整体普通型(非保温)、整体保温型(内、外表面为无机玻璃钢,中间为绝热材料)、组合型(由复合板、专用胶、法兰、加固角件等连接成风管)和组合保温型四类,其制作参数应符合表 1、 2、 3的规定。
Inorganic glass steel wind pipe is divided into general general type (non thermal insulation), overall thermal insulation type (the inner and outer surface is inorganic glass steel, the middle is adiabatic material), combined type (the composite plate, special adhesive, flange, reinforcement angle parts etc. connected to the wind pipe) and combined heat insulation type four types, the parameters should be in accordance with the provisions of Table 1, 2, 3.
玻璃纤维网格布相邻层之间的纵、横搭接缝距离应大于300mm,同层搭接缝距离不得小于500mm。搭接长度应大于50mm。
The distance between longitudinal and transverse joints between adjacent layers of glass fiber mesh cloth shall be greater than 300mm, and the distance between the joints of the same layer shall not be less than 500mm. The lap length should be greater than 50mm.
风管表层浆料厚度以压平玻璃纤维网格布为宜(可见布纹)。且表面不得有密集气孔和漏浆。
The thickness of the surface layer of the wind pipe is suitable for pressing the glass fiber mesh cloth (visible cloth). There are no dense pores and leakage of slurry on the surface.